コロナ ホウデン ショリ ニヨル モクザイ ノ ブッセイ ヘンカ
Title Alternative (English)
Effect of corona treatment on wood properties
File
language
jpn
Author
Uehara, Tohru
Goto, Teruo
Description
Infrared spectrum, JIS color difference and tensile strength of corona treated wood were measured and fracture texture was obseryed, to investigate the effect of corona treatment on wood properties. The experiment was done using Hinoki(Chamaecyparis obtusa ENDL.) of strip and quarter sawn panel of which thickness were 30μm and 2.5mm respectwely. For electrode, gap was 7mm, and applied voltage was from 9 to 15 kV, 60Hz, in nitrogen or air.
The absorbance of carbonyl group(1730cm^<-1>) increased with an increase in the degree of corona treatment in spite of the corona discharging atmosphere. It was considered that the post oxidation occured in the nitrogen corona.
It was expected that the surface roughness of wood increased with an increase in the JIS color difference, but that was not confirmed with the secondary electron images.
The tensile strength of wood strip decraesed linearly with an increase in the square root of the degree of treatment. By the observation of fracture texture, it was also shown that the longitudinal strength of cell wall decreased.
Journal Title
Bulletin of the Faculty of Agriculture, Shimane University
Volume
19
Start Page
57
End Page
64
ISSN
0370940X
Published Date
1985-12-20
NCID
AN00108015
Publisher
島根大学農学部
Publisher Aalternative
Shimane University, Faculty of Agriculture
NII Type
Departmental Bulletin Paper
OAI-PMH Set
Faculty of Life and Environmental Science
他の一覧
このエントリーをはてなブックマークに追加