The Relationship between Span-Depth Ratio and Bending Characters of Wood Beam
ファイル
言語
日本語
著者
高橋 徹
桜井 敏夫
内容記述(抄録等)
This paper deals with the characteristics of bending strength i. e. the modulus of bending rupture, stress value at propotional limit, shearing stress and the modulus of elasticity in bending, when the span-to-depth ratio of wooden beam is varied from 2 to 20. In case of a simply supported beam that carries a concentrated load P at midspan, as Figure 1 indicates, the results of the experiments are shown in Figure 2 through 5.
On the basis of the results, it can be concluded as follows :
(1) Figure 2 illustrates the similar tendency to the modulus of bending rupture between HINOKI and RED LAUAN, except that the span-to-depth ratio of 6 of HINOKI beam makes a maximum, that while that of RED LAUAN does not show the maximum. It demonstrates, furthermore, such a phenomenon of the modulus of bending rupture is affected by the compressive strength perpendicular to grain, and by species, etc.
(2) In Fig. 3, it can be seen that the stress at proportional limit of bending increases as the span-to-depth ratio of beam increases, and a single curve is drawn through all of the points to emphasize the similar behavior of HINOKI and RED LAUAN beams tested. The author can infer that the span-to-depth ratio is dependent on the normal distribution of internal stress in beam.
(3) The shearing strength is affected by the span-to-depth ratio of the wooden beam. As the span-to-depth ratio is increased, it is observed generally that the shearing strength decreased.
(4) Table 2 illustrates the strength properties of HINOKI and RED LAUAN beams and comparison on an average (av.) and deviation (dev.) of the measured and calculated bending strength. The measured bending strength of beam specimens agrees resonably well with those computed, as a whole, falling in the range from 0.83 to 1.11. And Table 3 shows the distribution of the shearing stress to the modulus of bending rupture.
掲載誌名
島根農科大学研究報告
15
開始ページ
(A-2)34-40
ISSN
05598311
発行日
1967-01-31
NCID
AN00108241
出版者
島根農科大学
出版者別表記
The Shimane Agricultural College
資料タイプ
紀要論文
部局
生物資源科学部
備考
A,Bを含む
開学十五周年記念号(Commemoration Issue for the 15th Aniversary)
他の一覧
このエントリーをはてなブックマークに追加