Optical Microscopy and Scanning Electron Microscopy of Sekishu Clay Rooftiles
c0040030r001.pdf 12.8 MB
Optical and Scanning Electron Microscopic investigations were performed for clay rooftiles produced at Gotsu of Shimane in Japan. The clay rooftiles have been traditionally called 'Sekishu Kawara' and famous for their high quality. It has about 25% shear of all Japanese product. Before firing in a tunnel kiln, the clay rooftiles consist of Kaolinite (Al_2Si_20_5(OH)_4) and quartz. They show lamella structures. After the firing at 1493 K ( 1220℃), however, they change to mullite and several Si0_2 related materials. The lamella structures disappear.
From the X-ray diffraction analysis, chemical formula for the firing reaction would be 3Al_2Si_20_5(OH)_4→Al_6Si_2O_13+4H_20 + 6H_2O; that shows, kaolinite changes into mullite, cristobalite and water. As minorities, K, Na, Ca and Mg are detected all over the area and some types of oxides of Fe，Ti，Mn and Zr stud‘Kawara'．The result of the chemical analysis in this study is as follows: SiO_2 related materials 70.2%，mullite 22.3%，iron oxide 3.7% and others．
Microscopic images of the rooftiles exhibits extremely rough shape. Holes or tunnels with three dimensional complex figure are observed in the SEM images. The smallest diameter of the holes or tunnels in the rooftiles is 1 or 2 micrometers．These holes or tunnels would be open pores． On the other hand，the SiO_2 related materials show small closed pores whose diameteris in order of a tenth of one micrometer．The total volume of the holes or tunnels are estimated to be 24% of the whole volume of the rooftile．
Huge volume of vapour comes out of the clay during the firing at 1493 K in the tunnel kiln．The vapour would be one of the impotant factors in forming the complicated three dimensional figure in the mullite of the roofiles.