モクシツ ザイリョウ ノ カイリョウ ニ カンスル ケンキュウ ダイ5ホウ PMMA-HINOKI COMBINATION ノ キュウスイ キョドウ
日本語以外のタイトル
Studies on the Improvement of Wooden Materials(V) : Behavio of Water Absorption on PMMA-Hinoki Combination
ファイル
言語
日本語
著者
古野 毅
後藤 輝男
往西 弘次
内容記述(抄録等)
In this paper, the behavior of water absorption on PMMA-Hinoki combination(WPC) has been investigated, following the hygroscopicity experiment of the previous report (IV).
The specimens(10(R) ×50(T) ×5(L) mm) of Hinoki(Chamaecyparis Obtusa ENDL.) were impregnated with methy methacrylate(MMA), using various treatment conditions, and cured by the catalyst-heat technique as described in the previous report.
The ASE(anti-swelling efficiency) measurements were made on vacuum-dry and water-soaked specimens. The specimens were allowed to soak until equilibrium swelling was reached. The dimensional change in tagential direction were then measured and the ASE was calculated.
The results obtained are as follows :
The behavior of water absorption on WPC shows a different phenomenon from that of hygroscopicity. Namely, the results concerning the relation between ASE and polymer content(Fig. 3) showed a tendency approximately similar to those of Loos' study. Although an inverse proportional relation between polymer content and water absorption is obtained(Fig. 2), at higher polymer content the ASE values tend to drop off and show values near to zero. As the reason for this, it is assumed that at high polymer content the specimens shrink due to the shrinkage of the monomer during polymerization, and thus during swelling this shrinkage stress is relieved causing greater than normal swelling.
掲載誌名
島根大学農学部研究報告
4
開始ページ
110
終了ページ
112
ISSN
0370940X
発行日
1970-12-15
NCID
AN00108015
出版者
島根大学農学部
出版者別表記
Shimane University, Faculty of Agriculture
資料タイプ
紀要論文
部局
生物資源科学部
他の一覧